Chromatic analysis of orthodontic resin bonding agents exposed to different antiseptic mouthrinses

ABSTRACT Objective: To assess the color of different orthodontic resin bonding agents exposed to three antiseptic mouthrinses for a prolonged time interval (10-year aging simulation). Methods: 160 specimens were distributed into four groups, according to the orthodontic resin bond agent (Concise, Transbond XT, Transbond Plus Color Change, and Natural Ortho). Each group was exposed to different antiseptic mouthrinses: alcohol-based (Listerine®), alcohol-free (Oral-B®), chlorhexidine (Periogard®) and distilled water as the control. Specimens were submitted to two cycles of staining and artificial aging. Color was evaluated by means of a digital spectrophotometer at the beginning of the experiment and after every cycle. The system used to assess color changes was the CIE L*a*b*. Data was analyzed using the ANOVA and Tukey post-hoc test. Results: After simulation of 10 years of aging, Transbond XT and Natural Ortho composites presented no statistically significant differences in ∆E when exposed to different mouthrinses. The Concise composite specimens exposed to alcohol-free mouthrinse presented a significant difference when compared with specimens from the same group exposed to other antiseptic mouthrinses. Transbond Plus Color Change specimens exposed to chlorhexidine mouthrinse and to alcohol-containing mouthrinse presented a significant difference when compared with the specimens from the group exposed to water and alcohol-free antiseptic. Conclusion: All orthodontic resin bonding agents tested presented clinically perceptible color changes when exposed to at least one of the mouthrinses, except for the Natural Ortho composite. The Concise composite exposed to the alcohol-free solution was the resin that presented the highest color change values.

RESUMO Objetivo: Avaliar a cor de diferentes resinas ortodônticas expostas a três enxaguantes bucais, por um intervalo de tempo prolongado (simulação de 10 anos de envelhecimento). Métodos: 160 espécimes foram distribuídos em quatro grupos, de acordo com a resina de colagem ortodôntica (Concise, Transbond XT, Transbond Plus Color Change e Natural Ortho). Cada grupo foi exposto a diferentes tipos de enxaguantes bucais: à base de álcool (Listerine®), isento de álcool (Oral-B®), clorexidina (Periogard®) ou água destilada, como controle. Os espécimes foram submetidos a dois ciclos de manchamento e envelhecimento artificial. A cor foi avaliada por meio de um espectrofotômetro digital no início do experimento e após cada ciclo. O sistema utilizado para avaliar as alterações de cor foi o CIE L*a*b*. Os dados foram analisados utilizando-se o teste ANOVA e o teste post-hoc de Tukey. Resultados: Após a simulação de 10 anos de envelhecimento, as resinas Transbond XT e Natural Ortho não apresentaram diferenças estatisticamente significativas no ∆E, quando expostas a diferentes enxaguantes bucais. Os espécimes do grupo Concise expostos ao enxaguante bucal sem álcool apresentaram diferença significativa quando comparados aos espécimes do mesmo grupo expostos aos outros enxaguantes bucais. Os espécimes do grupo Transbond Plus Color Change expostos à clorexidina e ao enxaguante bucal à base de álcool apresentaram diferença significativa quando comparados aos espécimes dos grupos expostos à água e ao enxaguante bucal sem álcool. Conclusão: Todas as resinas ortodônticas avaliadas apresentaram alterações de cor clinicamente perceptíveis quando expostas a pelo menos um dos enxaguantes bucais, com exceção da resina ortodôntica Natural Ortho. A resina Concise exposta à solução isenta de álcool foi a que apresentou os maiores valores de alteração de cor.

Alteração de cor em simulação de dente escurecido, utilizando duas resinas compostas de mesma cor com diferentes opacidades / Colour change in a simulation of discolored tooth using two composite resins of the same colour but different opacities

Introdução: o tratamento estético de dentes escurecidos é desafiador, especialmente quando o escurecimento ocorre de maneira pontual. Para alcançar bons resultados, é imprescindível, além do domínio da técnica restauradora, o conhecimento sobre a composição e características ópticas dos materiais restauradores. Objetivo: avaliar a cor resultante da sobreposição de duas resinas compostas, quando utilizadas sobre um substrato escurecido. Metodologia: na confecção dos corpos de prova, foram utilizadas duas matrizes metálicas e as resinas compostas Charisma A2 e OA2 e Opallis DA4 (simulando o substrato escurecido), perfazendo um total de 30 corpos de prova. As mensurações de cor foram realizadas em espectrofotômetro de reflexão (UV-2600; Shimadzu) e as leituras colorimétricas foram realizadas no programa Color Analysis, seguindo os parâmetros do sistema CIEL*a*b*. A análise estatística inferencial foi realizada pela ANOVA 1-critério. Para as comparações múltiplas, utilizou-se o teste Tukey (significância de 5%). Resultados: entre as três variáveis, apenas na variável a* houve diferença estatística (p<0,0001). Conclusão: os resultados permitiram a observação de alteração colorimétrica após o uso de ambas as resinas, porém com melhores resultados para o grupo da resina AO2, quando em comparação com o grupo da A2.

Introduction: the aesthetic treatment of darkened teeth is challenging, especially when darkening occurs in a timely manner. Besides mastering the restorative technique, knowledge about the composition and optical characteristics of restorative materials are essential in order to achieve good results. Objective: to evaluate the colour resulting from the overlapping of two composite resins when used on a darkened substrate. In the preparation of the test specimens, two metal matrices and the Charisma A2 and OA2 and Opallis DA4 composite resins (simulating the darkened substrate) were used, making a total of 30 specimens. The color measurements were performed in a spectrophotometer (UV-2600; Shimadzu) and the colorimetric readings were performed in the Color Analysis program, following the CIEL * a * b * system parameters. Inferential statistical analysis was carried out by ANOVA 1-criterion. The Tukey test (5% significance) was used for the multiple comparisons. Results: among the three variables, only in variable a * there was a statistical difference (p <0.0001). Conclusion: the results allowed the observation of colorimetric alteration after the use of both resins, but with better results for the AO2 resin group in comparison to the A2 group.

Effect of thickness on fluorescence of resin composites and dental substrates / Efeito da espessura sobre a fluorescência de resinas compostas e substratos dentais

Objective: This study evaluated the effect of thickness on fluorescence of resin composites and tooth substrates (enamel and dentin). Material and methods: Ninety bovine incisors were used, resulting in 45 dentin and 45 enamel disks (6 mm diameter and 0.5, 1, or 1.5 mm in thickness). Ninety discs of Charisma, Filtek Z350 and IPS Empress Direct (for enamel and dentin) resins at same dimensions were built. Fluorescence measurements were performed using a fluorescence spectrophotometer (RF-5301PC, Shimadzu Corp) with excitation at 365 nm. Data were submitted to 2-way ANOVA and Tukey’s post hoc tests (α = 0.05). Results: The 2-way ANOVA revealed statistically significant differences for all factors, as well as the interaction between them (p <0.05). Dentin specimens (1.5 mm) showed highest fluorescence (128.33 A.U.), while Filtek Z350 (dentin - 1.0 mm) showed the lowest fluorescence (29.84 A.U.). Thickness influenced fluorescence values of enamel substrate. Conclusion: The thickness influenced fluorescence of enamel and all resin composite assessed showed fluorescence lower than natural dentin.

Objetivo: Este estudo avaliou o efeito da espessura de resinas compostas e substratos dentais (esmalte e dentina) sobre a fluorescência. Materiais e Métodos: Noventa incisivos bovinos foram utilizados, resultando em 45 discos de dentina e 45 discos de esmalte (6 mm de diâmetro e 0,5, 1 ou 1,5 mm mm de espessura). Noventa discos das resinas compostas Charisma, Filtek Z350 e IPS Empress Direct (para esmalte e dentina) foram confeccionados com a mesma dimensão. A fluorescência foi analisada por meio de espectrofluorímetro (RF-5301PC, Shimadzu Corp) com excitação de 365nm. Os dados foram submetidos ao teste ANOVA dois fatores e Teste de Tukey (α = 0,05). Resultados: O teste ANOVA dois fatores revelou diferenças significativas para todos os fatores, bem como para interação entre eles (p < 0,05). As amostras de dentina (1,5 mm) apresentaram alta fluorescência (128,33 A.U.), enquanto a resina composta Filtek Z350 (dentina - 1,0 mm) apresentou menor fluorescência (29,84 A.U.). A espessura influenciou os valores de fluorescência para o substrato esmalte. Conclusão: A espessura influenciou na fluorescência do esmalte e todas as resinas compostas avaliadas apresentaram uma fluorescência menor do que a dentina natural.

Effect of the photoinitiator system on the properties of a dental material based on a hybrid polymer / Efeito do sistema fotoiniciador sobre as propriedades de um material dentário baseado em um polímero híbrido

Objetivo: Nesse estudo, foram avaliados os efeitos de dois diferentes protocolos de cura sobre as propriedades de um compósito usando um polímero híbrido como resina dentária. Material e Métodos: Dois compósitos diferentes foram preparados, um contendo uma mistura de TEGDMA/Bis-GMA (50:50) e, outro contendo uma mistura de TEGDMA/p-MEMO (50:50), [p-MEMO: precursor oligomérico inorgânico]. Ambos compósitos foram reticulados com lucirin e canforoquinona. Os compósitos foram preparados com 70% em massa de carga inorgânica. Resistência flexural foi avaliada com uma máquina de testes universal e o grau de conversão calculado por espectroscopia na região do infravermelho. Um picnômetro a gás hélio foi usado para obter os dados de contração de polimerização. Testes de sorção foram feitos e microscopia eletrônica de varredura foi usada para avaliar efeitos deletérios sobre as superfícies das resinas. Resultados: A amostra constituída com TEGDMA/p-MEMO reticulada com lucirin (L-T/p) apresentou os melhores valores das propriedades monitoradas. Conclusão: Lucirin é o sistema fotoiniciador mais adequado para compostos dentários contendo polímeros híbridos.

Objective: In this study, the effects of two different cure protocols upon the properties of composites using a hybrid-polymer as dental resin were evaluated. Material and Methods: Two distinct dental composites were prepared, one containing a mixture of TEGDMA/bis-GMA (50:50) and, another containing a mixture of TEGDMA/p MEMO (50:50), [p-MEMO: oligomeric inorganic precursor]. Both composites were polymerized with lucirin and canphorquinone as photoinitiators. The composites were made with a 70 % wt of inorganic filler. Flexural strength was evaluated with a universal test machine and the degree of conversion was measured by infrared spectroscopy. A helium pycnometer was used to obtain polymer shrinkage data. Sorption tests were performed and SEM microscopy was used to show deleterious effects upon the resins’ surfaces. Results: The sample based on TEGDMA/p-MEMO polymerized with lucirin (L-T/p) showed the best values of the monitored properties. Conclusion: Lucirin is the most suitable photoinitiator for dental composites containing hybrid polymers.

Effect of activation mode on flexural strength in dual-polymerized resin cements / Efeito do modo de ativação na resistência a flexão de cimentos resinosos duais

Objective: To compare he influence of two activation modes on two similar dual-polymerized resin cements. Methods: Bars (2 × 2 × 12 mm) of RelyX ARC (3M ESPE, MN, USA) (ARC) and Enforce (Dentsply, Rio de Janeiro, Brazil) (ENF) were prepared, and three types of polymerization method were tested: (1) L: LED photoactivation/40 s; (2) H: halogen Light activations/40 s, and (3) C: chemical activation only (Complete absent of light). The groups were ARC-L; ARC-H, ARC-C, Enf-L, Enf-H, and Enf-C (n = 8). After 24 h, the specimens were tested using the 3-point bending method on a universal testing machine. Results: The ARC cement showed superior flexural strength results. The mode of activation revealed similar results on both cements tested, but lightactivated groups (with LED or Halogen light) showed higher flexural strength values than did the chemical-activation-only group. Conclusion: (1) RelyX ARC cement showed superior flexural strength when compared with Enforce; and (2) light activation resulted in better flexural strength values when compared to chemical activation on dual-polymerized resin cements.

Objetivo: Comparar a influência do modo de ativação de dois cimentos semelhantes, porém de fabricantes distintos. Métodos: Barras (2 x 2 x 12 mm) dos cimentos RelyX ARC (3M ESPE, MN, USA) e Enforce (Dentsply, Rio de Janeiro, Brasil) (ENF) foram confeccionadas com auxílio de uma matriz de teflon bipartida, e três modos de fotopolimerização foram testados: (1) L: fotoativação por LED / 40 segundos; (2) H - fotoativação por luz halógena / 40 segundos; e (3) Q - apenas ativação química (ausência total de luz). Os grupos formados foram: ARC-L; ARC-H; ARC-Q; Enf-L; Enf-H e Enf-Q, com 8 amostras cada. Após 24 horas, o teste de miniflexão de três pontos foi aplicado em máquina universal de testes. Resultados: O cimento ARC apresentou resultados de resistência superiores ao cimento Enf. O modo de ativação agiu de forma semelhante nos dois cimentos testados, sendo que a ativação por luz, seja L ou H, aumentou a resistência para ambos, comparada a ativação Q. Conclusão: (1) O cimento RelyX ARC (3M ESPE, MN, USA) apresentou maior resistência à flexão de três pontos quando comparado ao cimento Enforce(Dentsply, Rio de Janeiro, Brasil); e (2) a ativação por luz aumentou a resistência para cimentos resinosos duais.